Water bearing adhesive sealing tape with high adhesion strength
- Protects structural elements from water ingress: watertight and blocks rising damp
- Extremely high adhesion even to slightly damp and cold surfaces
- Very elastic: can adapt flexibly to subsurfaces and corners
- Bonds to mineral substrates
- Seals nail holes
- Lowest VOC rating in hazardous substance test
Watertight adhesive tape with high adhesion for creating self sealing sill flashing, for joining wood-based panels to smooth mineral surfaces, to stick sub-roof panels one below the other (e.g. in grooves and transitions) and to bond these to adjoining structural elements.
|Backing||elastic PE carrier film|
|Material||Butyl rubber modified with acrylate|
|Release film||silicone-coated PE film|
|Colour||Butyl rubber: grey, film: black|
|Surface weight||EN 1849-2||approx. 1.9 kg/m²||EN 1849-2|
|Thickness||EN 1849-2||approx. 1.1 mm||EN 1849-2|
|sd-value||EN 1931||> 100 m||EN 1931|
|g-value||> 500 MN·s/g|
|Vapor permeance||ASTM E 96||< 0.03 US perms||ASTM E 96|
|Exposure time||6 months|
|Resistance to driving rain||ift, MO-01/1:2007-01, Abs. 5||up to 600 Pa, self sealing sill flashing||ift, MO-01/1:2007-01, Abs. 5|
|Application temperature||-10 °C to 35 °C ; 14 °F to 95 °F|
|Temperature resistance||permanent -40 °C to 80 °C ; -40 °F to 176 °F|
|Storage||cool and dry|
The bonds should not be subjected to tensile strain.
Press firmly to secure the adhesive tape. Ensure there is sufficient back pressure.
Windproof, airtight or rainproof seals can only be achieved on vapour retarding membranes, roof lining membranes or façade membranes that have been laid without folds or creases.
The tape is self-bonding under the effect of heat.
Before sticking, subsurfaces should be brushed off, wiped clean with a cloth or cleaned using compressed air.
Adhesion to frozen surfaces is not possible. There must be no water-repellent substances (e.g. grease or silicone) on materials to be bonded. Subsurfaces must be sufficiently dry and have sufficient load-bearing capacity.
Permanent adhesion is achieved on woodbased panels (chipboard, OSB and veneer plywood, MDF board and wood fibre sub-roof panels).
Wood fibre sub-roof panels and smooth mineral subsurfaces require pre-treatment with TESCON PRIMER before bonding. Concrete or plaster subsurfaces must not be sandy or crumbling.
The best results in terms of structural stability are achieved on high-quality subsurfaces.
It is your responsibility to check the suitability of the subsurface; adhesion tests are recommended in certain cases.
Pretreatment with TESCON PRIMER is recommended in the case of subsurfaces with insufficient load-bearing capacity.